| 1. Identificação | |
| Tipo de Referência | Artigo em Revista Científica (Journal Article) |
| Site | mtc-m16.sid.inpe.br |
| Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S |
| Identificador | 6qtX3pFwXQZGivnJVY/Mc8Kt |
| Repositório | sid.inpe.br/mtc-m16@80/2006/08.18.18.04 (acesso restrito) |
| Última Atualização | 2006:08.18.18.04.14 (UTC) marciana |
| Repositório de Metadados | sid.inpe.br/mtc-m16@80/2006/08.18.18.04.15 |
| Última Atualização dos Metadados | 2018:06.05.01.17.04 (UTC) administrator |
| Chave Secundária | INPE-14064--PRE/9233 |
| ISSN | 0093-3813 |
| Chave de Citação | SilvaUeSiCo:2006:EfHiPl |
| Título | Effects of the high-temperature plasma immersion ion-implantation treatment on corrosion behavior of Ti-6Al-4V  |
| Ano | 2006 |
| Mês | Aug. |
| Data de Acesso | 21 maio 2024 |
| Tipo Secundário | PRE PI |
| Número de Arquivos | 1 |
| Tamanho | 413 KiB |
| 2. Contextualização | |
| Autor | 1 Silva, Leide Lili Gonçalves 2 alves 3 Ueda, Má 4 rio 5 Silva, M. M. 6 Cordaro, E. N. |
| Grupo | 1 LAP-INPE-MCT-BR 2 LAP-INPE-MCT-BR |
| Afiliação | 1 Instituto Nacional de Pesquisas Espaciais, Laborató 2 rio Associado de Plasma (INPE.LAP) 3 Instituto Nacional de Pesquisas Espaciais, Laborató 4 rio Associado de Plasma (INPE.LAP) |
| Revista | IEEE Transactions on Plasma Science |
| Volume | 34 |
| Número | 4 part 1 |
| Páginas | 1141-1147 |
| Histórico (UTC) | 2006-08-18 18:12:13 :: simone -> administrator :: 2008-06-10 22:43:48 :: administrator -> simone :: 2011-05-29 00:47:37 :: simone -> administrator :: 2014-04-16 17:25:22 :: administrator -> marciana :: 2006 2014-08-20 18:42:59 :: marciana -> administrator :: 2006 2018-06-05 01:17:04 :: administrator -> marciana :: 2006 |
| 3. Conteúdo e estrutura | |
| É a matriz ou uma cópia? | é a matriz |
| Estágio do Conteúdo | concluido |
| Transferível | 1 |
| Tipo do Conteúdo | External Contribution |
| Tipo de Versão | publisher |
| Palavras-Chave | Corrosion hardness measurment ion implantation titanium alloys |
| Resumo | Nitrogen implantation into Ti alloys at higher temperatures improves their mechanical and corrosion resistance properties by forming a thicker nitride layer. In this paper, two different sets of Ti-6Al-4V samples were plasma immersion ion implantation (PIII)-treated using nitrogen plasma, varying the treatment time from 30 to 150 min (800¨¬C) and the process temperature from 400¨¬C to 800¨¬C (t = 60 min). Nanoindentation measurements of the PIII-treated samples at 800¨¬C during 150 min showed the highest hardness value, 24 GPa, which is about four times bigger than untreated sample hardness. The N penetration at these conditions reached approximately 150 nm as analyzed by Auger spectroscopy. On the other hand, the lowest passive current density (3 ¡¿ 10-7 A ¡¤ cm-2) was obtained for a PIII-treated sample during 30 min at higher temperature (800¨¬C). The corrosion resistance of this sample is almost the same as for the untreated specimen. Corrosion behavior evidenced that in strong oxidizing media, all PIII-treated samples are more corrosion resistant than the untreated one. PIII processing at higher temperatures promotes smoothing of the sample surface as observed by scanning electron microscopy (SEM). Grazing incidence X-ray diffraction analyses of the untreated samples identified the two typical Ti phases, Ti ¥á and Ti ¥â. After the implantation, Ti2N and TiO2 phases were also detected. |
| Área | FISPLASMA |
| Arranjo | urlib.net > BDMCI > Fonds > Produção anterior à 2021 > LABAP > Effects of the... |
| Conteúdo da Pasta doc | acessar |
| Conteúdo da Pasta source | não têm arquivos |
| Conteúdo da Pasta agreement | não têm arquivos |
| 4. Condições de acesso e uso | |
| Idioma | en |
| Arquivo Alvo | Effects of the high temperature plasma.pdf |
| Grupo de Usuários | administrator marciana simone |
| Grupo de Leitores | administrator marciana |
| Visibilidade | shown |
| Detentor da Cópia | SID/SCD |
| Política de Arquivamento | denypublisher allowfinaldraft |
| Permissão de Leitura | deny from all and allow from 150.163 |
| Permissão de Atualização | não transferida |
| 5. Fontes relacionadas | |
| Unidades Imediatamente Superiores | 8JMKD3MGPCW/3ET2RFS |
| Lista de Itens Citando | sid.inpe.br/bibdigital/2013/09.25.21.49 1 |
| Divulgação | WEBSCI; PORTALCAPES; COMPENDEX; IEEEXplore. |
| Acervo Hospedeiro | sid.inpe.br/banon/2003/08.15.17.40 |
| 6. Notas | |
| Campos Vazios | alternatejournal archivist callnumber copyright creatorhistory descriptionlevel doi e-mailaddress electronicmailaddress format isbn label lineage mark mirrorrepository nextedition notes orcid parameterlist parentrepositories previousedition previouslowerunit progress project resumeid rightsholder schedulinginformation secondarydate secondarymark session shorttitle sponsor subject tertiarymark tertiarytype typeofwork url |
| 7. Controle da descrição | |
| e-Mail (login) | marciana |
| atualizar | |